Substrate for epitaxial growth, and crystal laminate structure

ABSTRACT

Provided is a substrate for epitaxial growth, which enables the improvement in quality of a Ga-containing oxide layer that is formed on a β-Ga 2 O 3  single-crystal substrate. A substrate ( 1 ) for epitaxial growth comprises β-Ga 2 O 3  single crystals, wherein face (010) of the single crystals or a face that is inclined at an angle equal to or smaller than 37.5° with respect to the face (010) is the major face. A crystal laminate structure ( 2 ) comprises: the substrate ( 1 ) for epitaxial growth; and epitaxial crystals ( 20 ) which are formed on the major face ( 10 ) of the substrate ( 1 ) for epitaxial growth and each of which comprises a Ga-containing oxide.

TECHNICAL FIELD

The invention relates to an epitaxial growth substrate (or substrate for epitaxial growth) and, in particular, to an epitaxial growth substrate that includes a β-Ga₂O₃-based single crystal and a crystal laminate structure (or laminated crystal structure).

BACKGROUND ART

A semiconductor element is known in which a Ga-containing oxide is deposited on an element substrate formed of a β-Ga₂O₃-based single crystal (see, e.g., PTL 1).

This type of semiconductor element is formed by laminating a layer of n-type or p-type conductivity on a main surface of a β-Ga₂O₃ single crystal substrate using a physical vapor-phase growth method such as MBE (Molecular Beam Epitaxy) or a chemical vapor-phase growth method such as CVD (Chemical Vapor Deposition).

In addition, a (100) plane having high cleavability and thus providing a flat surface easily is used as the main surface of the β-Ga₂O₃ single crystal substrate (see, e.g., PTL 2).

CITATION LIST Patent Literature

[PTL 1]

JP-A-2005-235961

[PTL 2]

JP-A-2008-156141

SUMMARY OF INVENTION Technical Problem

Recently, for further improvement in performance of semiconductor elements, the challenge is how to form a steep interface between the element substrate and an epitaxial layer formed thereon and between laminated epitaxial layers and how to form an epitaxial layer with a highly accurate thickness.

It is an object of the invention to provide an epitaxial growth substrate that allows an improvement in the crystalline quality of a Ga-containing oxide layer formed on the β-Ga₂O₃ single crystal substrate, as well as a crystal laminate structure.

Solution to Problem

The present inventors have conducted researches for achieving the above object and found that the crystalline quality of the Ga-containing oxide layer formed on the β-Ga₂O₃ single crystal substrate depends on which crystal surface of the β-Ga₂O₃ single crystal substrate is used as the main surface. Then, the present invention has been completed by repeating further experiments.

The present invention is based on findings obtained by the experiments and offers the epitaxial growth substrate and the crystal laminate structure below.

[1] An epitaxial growth substrate, comprising:

-   -   a β-Ga₂O₃-based single crystal; and     -   a (010) plane or a plane inclined at an angle not more than         37.5° with respect to the (010) plane as a main surface thereof.

[2] The epitaxial growth substrate according to [1], wherein the main surface comprises a (010) plane or a plane between the (010) plane and a (310) plane of the β-Ga₂O₃-based single crystal.

[3] The epitaxial growth substrate according to [2], wherein the main surface comprises the (010) plane or the (310) plane of the β-Ga₂O₃-based single crystal.

[4] A crystal laminate structure, comprising:

-   -   an epitaxial growth substrate comprising a β-Ga₂O₃-based single         crystal and a (010) plane or a plane inclined at an angle not         more than 37.5° with respect to the (010) plane as a main         surface thereof; and     -   an epitaxial crystal formed on the main surface of the epitaxial         growth substrate and comprising a Ga-containing oxide.

[5] The crystal laminate structure according to [4], wherein the main surface comprises a (010) plane or a plane between the (010) plane and a (310) plane of the β-Ga₂O₃-based single crystal.

[6] The crystal laminate structure according to [5], wherein the main surface comprises the (010) plane or the (310) plane of the β-Ga₂O₃-based single crystal.

Advantageous Effects of Invention

According to an embodiment of the invention, the crystalline quality of the Ga-containing oxide layer formed on the β-Ga₂O₃ single crystal substrate can be improved.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1A is a perspective view showing an epitaxial growth substrate in a first embodiment.

FIG. 1B is a sterical view showing a crystal structure by which the plane orientation of the epitaxial growth substrate of FIG. 1A is defined.

FIG. 2 is a cross sectional view showing an example structure of a crystal laminate structure.

FIG. 3 is a cross sectional view showing an MBE system used for forming the crystal laminate structure.

FIG. 4A is an XRD 2θ-θ spectrum showing an X-ray diffraction measurement result of the crystal laminate structure when only one (AlGa)₂O₃ layer with an Al content of 20% is epitaxially grown on the epitaxial growth substrate.

FIG. 4B is an atomic force microscope image showing a surface state of an epitaxial crystal.

FIG. 5A is a TEM observation image of a crystal laminate structure in which plural (AlGa)₂O₃ layers and Ga₂O₃ layers are alternately formed.

FIG. 5B is an XRD 2θ-θ spectrum of the crystal laminate structure.

FIG. 6A is an atomic force microscope image showing a surface state of an epitaxial crystal which is shown as a Comparative Example and is grown so as to have a (100) plane as a main surface.

FIG. 6B is an atomic force microscope image showing a surface state of an epitaxial crystal which is shown as a Comparative Example and is grown so as to have a (001) plane as a main surface.

FIG. 7A is a TEM observation image of a crystal laminate structure in which plural (AlGa)₂O₃ layers and Ga₂O₃ layers are alternately formed on an epitaxial growth substrate formed of a β-Ga₂O₃-based single crystal having a (100) plane as a main surface.

FIG. 7B is an XRD 2θ-θ spectrum of the crystal laminate structure of FIG. 7A.

FIG. 8A is a perspective view showing an epitaxial growth substrate in a modification of the first embodiment.

FIG. 8B is a sterical view showing a (310) plane of the β-Ga₂O₃-based single crystal.

FIG. 8C is a diagram illustrating an angle δ defined between the (310) plane and the (010) plane of the β-Ga₂O₃-based single crystal.

FIG. 9 is an atomic force microscope image obtained when observing a surface of an epitaxial crystal formed on the (310) plane of the epitaxial growth substrate.

FIG. 10 is a cross sectional view showing an example structure of a high-electron-mobility transistor in a second embodiment of the present invention.

FIG. 11 is a cross sectional view showing an example structure of a MESFET in a third embodiment of the invention.

FIG. 12 is a cross sectional view showing an example structure of a Schottky-barrier diode in a fourth embodiment of the invention.

DESCRIPTION OF EMBODIMENTS

FIG. 1A is a perspective view showing an epitaxial growth substrate in the first embodiment of the invention. This epitaxial growth substrate 1 is formed of a β-Ga₂O₃ (gallium oxide)-based single crystal and has a (010) plane as a main surface 10.

The epitaxial growth substrate 1 is formed in a plate shape having predetermined plane orientations. Orientation axes of the β-Ga₂O₃ crystal structure includes an a-axis <100>, a b-axis <010> and a c-axis <001>, and the epitaxial growth substrate 1 is formed in a plate shape having the predetermined plane orientations defined by these three axes, i.e., a (010) plane, a (100) plane and a (001) plane. Of those, the (010) plane is the main surface 10 used for epitaxially growing a crystal of Ga-containing oxide when manufacturing a semiconductor element and is formed so as to have a larger area than other planes.

FIG. 1B is a sterical view showing a crystal structure in which plane orientations of the epitaxial growth substrate of FIG. 1A are defined. β-Ga₂O₃ is a monoclinic crystal and is formed so that α=γ=90°, β=103.8°, a-axis lattice constant (a₀)=12.23 Å, b-axis lattice constant (b₀)=3.04 Å and c-axis lattice constant (c₀)=5.8 Å.

It should be noted that, the epitaxial growth substrate 1 is basically formed of β-Ga₂O₃ single crystal as described above but may be formed of an oxide including mainly Ga doped with one or more elements selected from the three consisting of Cu, Ag, Zn, Cd, Al, In, Si, Ge and Sn. It is possible to control a lattice constant, bandgap energy or electrical conduction properties by adding such elements. When adding, e.g., elements of Al and In, it is possible to obtain the epitaxial growth substrate 1 represented by (Ga_(x)Al_(y)In(_(1-x-y)))₂O₃ (where 0<x≦1, 0≦y≦1, 0<x+y≦1). The band gap is widened by adding Al and is narrowed by adding In.

(Method of Manufacturing Epitaxial Growth Substrate 1)

For manufacturing the epitaxial growth substrate 1, a bulk crystal is firstly made by the FZ (Floating Zone) method or the EFG (Edge Defined Film Fed Growth) method, etc., and is then cut out and formed into a plate shape by cutting or cleaving.

In case of using the FZ method, a bulk crystal is formed using, e.g., an infrared-heating single crystal manufacturing system. In detail, firstly, an end of a seed crystal is held on a seed chuck and an upper end portion of a rod-like polycrystalline raw material is held on a raw-material chuck. After adjusting a vertical position of an upper rotating shaft, the top edge of the seed crystal is brought into contact with the lower edge of the polycrystalline raw material. The vertical position of the upper rotating shaft and that of a lower rotating shaft are adjusted so that light of halogen lamp is focused on the upper edge of the seed crystal and the lower edge of the polycrystalline raw material. After the adjustment, the upper edge of the seed crystal and the lower edge of the polycrystalline raw material are heated the heated portion is melted, thereby forming melt droplets. At this time, only the seed crystal is being rotated. The aforementioned portion is melted while rotating the polycrystalline raw material and the seed crystal in opposite directions so as to be mixed sufficiently and the polycrystalline raw material and the seed crystal are then pulled in directions opposite to each other to form a single crystal having appropriate length and thickness, thereby making a bulk crystal.

In case of using the EFG method, a predetermined amount of β-Ga₂O₃ to be a raw material is put in a crucible and is melted by heating, thereby forming β-Ga₂O₃ melt. Through a slit formed on a slit die which is placed in the crucible, the β-Ga₂O₃ melt is drawn up to an upper surface of the slit die by capillary action, the β-Ga₂O₃ melt is cooled by contact with the seed crystal and a bulk crystal having an arbitrary cross sectional shape is thereby formed.

It should be noted that, the β-Ga₂O₃ bulk crystals made by these methods may be doped with impurities for the purpose of obtaining a desired conductivity type.

The β-Ga₂O₃ bulk crystal formed as described above is shaped by, e.g., a wire saw so that the (010) plane is exposed as a main surface, thereby obtaining thin sheet-like β-Ga₂O₃ having a desired shape with a thickness of, e.g., 1 mm. After grinding and polishing until the thickness becomes about 600 μm, the epitaxial growth substrate 1 is obtained.

Subsequently, the epitaxial growth substrate 1 is subjected to organic cleaning in order of methanol, acetone and methanol for three minutes each and is further subjected to running water cleaning using ultrapure water, hydrofluoric acid immersion cleaning for fifteen minutes, sulfuric acid/hydrogen peroxide mixture immersion cleaning for five minutes and then running water cleaning using ultrapure water. After the subsequent thermal cleaning at 800° C. for ten minutes, the main surface of the epitaxial growth substrate 1 is ready for epitaxial growth of a Ga-containing oxide.

(Crystal Laminate Structure and Forming Method Thereof)

Next, a crystal laminate structure and a forming method thereof in the present embodiment will be described in reference to FIGS. 2 and 3.

FIG. 2 is a cross sectional view showing an example structure of a crystal laminate structure in the present embodiment. A crystal laminate structure 2 is formed by laminating an epitaxial crystal 20 made of a Ga-containing oxide on the main surface 10 of the epitaxial growth substrate 1 described above.

The epitaxial crystal 20 is a crystalline body having, e.g., a β-Gallia structure containing Ga, and in more detail, is a crystalline body including mainly Ga₂O₃ or a mixed crystalline body containing Ga₂O₃ and more than 0 wt % and not more than 60 wt % of Al₂O₃ in the form of a crystal layer mainly having a β-Gallia structure. In addition, an impurity determining a conductivity type may be added to the epitaxial crystal 20.

The method of forming the epitaxial crystal 20 on the main surface 10 of the epitaxial growth substrate 1 is, e.g., PLD (Pulsed Laser Deposition), CVD (Chemical Vapor Deposition), sputtering and MBE (Molecular Beam Epitaxy) etc. In the present embodiment, a thin film growth method using the MBE is employed. The MBE is a crystal growth method in which a single or compound solid is heated in an evaporation source called cell and vapor generated by heat is supplied as a molecular beam onto the surface of the substrate.

FIG. 3 is a cross sectional view showing an MBE system used for forming the crystal laminate structure 2. An MBE system 3 is provided with a vacuum chamber 30, a substrate holder 31 supported in the vacuum chamber 30 to hold the epitaxial growth substrate 1, heating devices 32 held on the substrate holder 31, plural cells 33 (33 a, 33 b, 33 c, 33 d) each provided for each atom or molecule constituting the epitaxial crystal 20, heaters 34 (34 a, 34 b, 34 c, 34 d) for hearing the plural cells 33, a gas supply pipe 35 for supplying oxygen gas into the vacuum chamber 30, and a vacuum pump 36 for exhausting the air in the vacuum chamber 30. It is configured that the substrate holder 31 can be rotated by a non-illustrated motor via a shaft 310.

Ga to be a material of the epitaxial crystal 20 is loaded in the first cell 33 a. Al also to be a material of the epitaxial crystal 20 is loaded in the second cell 33 b. Meanwhile, a material to be doped as a donor, such as Si or Sn, is loaded in the third cell 33 c. A material to be doped as an acceptor, such as Mg or Zn, is loaded in the fourth cell 33 d. Each of the first to fourth cells 33 a to 33 d is provided with a non-illustrated shutter and is configured to be closed by the shutter when not necessary.

Next, a manufacturing procedure of the crystal laminate structure 2 will be described. Firstly, the epitaxial growth substrate 1 is attached to the substrate holder 31 of the MBE system 3. Next, the vacuum pump 36 is activated to reduce atmospheric pressure in the vacuum chamber 30 to about 10⁻¹⁰ Torr. Then, the epitaxial growth substrate 1 is heated by the heating devices 32.

After the epitaxial growth substrate 1 is heated to a predetermined temperature, oxygen gas produced by a non-illustrated oxygen generator is supplied into the vacuum chamber 30 through the gas supply pipe 35.

In case of making a crystal formed of Ga₂O₃ as the epitaxial crystal 20, the first heater 34 a of the first cell 33 a is heated while rotating the substrate holder 31 after supplying the oxygen gas into the vacuum chamber 30 so that Ga vapor is started to be supplied.

Meanwhile, in case of making a mixed crystal of Ga₂O₃ and Al₂O₃ as the epitaxial crystal 20, the first heater 34 a of the first cell 33 a and the second heater 34 b of the second cell 33 b are heated while rotating the substrate holder 31 so that Ga vapor and Al vapor are started to be supplied.

Growth conditions of the epitaxial crystal 20 in case of making a crystal formed of Ga₂O₃ as the epitaxial crystal 20 are, e.g., a growth temperature of 700° C., Ga beam-equivalent pressure (BEP) of 3×10⁻⁵ Pa and growth time of 1 hour. Meanwhile, in case of making a mixed crystal of Ga₂O₃ and Al₂O₃ as the epitaxial crystal 20, some of the above-mentioned growth conditions can be such that the Ga beam-equivalent pressure is 1.5×10⁻⁵ Pa and Al beam-equivalent pressure is, e.g., 5×10⁻⁷ Pa.

Accordingly, the epitaxial crystal 20 formed of a Ga-containing oxide is grown on the main surface 10 of the epitaxial growth substrate 1 and the crystal laminate structure 2 is thereby obtained.

Meanwhile, when imparting an n-type conductivity to the epitaxial crystal 20, the material to be a donor such as Si or Sn is supplied from the third cell 33 c by heating the third heater 34 c. On the other hand, when imparting a p-type conductivity, the material to be an acceptor such as Mg or Zn is supplied from the fourth cell 33 d by heating the fourth heater 34 d.

(Analysis of Crystal Laminate Structure)

FIG. 4A is an XRD (X-ray diffraction) 2θ-Θ spectrum showing an X-ray diffraction measurement result of the crystal laminate structure 2 having the epitaxial crystal 20 which is manufactured by the method mentioned above so as to be constructed from one β-(AlGa)₂O₃ layer with the Al content of 20%. A vertical axis of this graph shows X-ray scattering intensity expressed in logarithm. This graph shows a peak 1 a due to the epitaxial growth substrate 1 and a sharp peak 20 a due to the epitaxial crystal 20. In addition, a clear fringe is seen between the peak 1 a and the peak 20 a. Based on this clear fringe pattern, it is confirmed that a crystal laminate structure having a steep interface is formed.

FIG. 4B is an atomic force microscope image showing a surface state of the epitaxial crystal 20 which is manufactured by the method mentioned above so as to be constructed from one β-(AlGa)₂O₃ layer with the Al content of 20%. An arrow-A in the drawing indicates a [100] direction of the epitaxial growth substrate 1. It is confirmed from this image that the epitaxial crystal 20 grows in a direction vertical or nearly vertical to the main surface 10 (the (010) plane) of the epitaxial growth substrate 1.

FIG. 5A is a Transmission Electron Microscope (TEM) observation image of a crystal laminate structure 2A in which plural (AlGa)₂O₃ layers 21 and plural Ga₂O₃ layers 22 are alternately formed by epitaxial growth on the main surface 10 of the epitaxial growth substrate 1. The shutters of the first cell 33 a and the second cell 33 b of the MBE system 3 are opened and closed to adjust the thicknesses of the (AlGa)₂O₃ layers 21 and the Ga₂O₃ layers 22 to predetermined thicknesses as well as to alternately laminate each layer, thereby forming the crystal laminate structure 2A.

As shown in the TEM observation image, the crystal laminate structure 2A has six 6 nm-thick (AlGa)₂O₃ layers 21 and five 4 nm-thick Ga₂O₃ layers 22 which are alternately laminated on the epitaxial growth substrate 1. The (AlGa)₂O₃ layers 21 and the Ga₂O₃ layers 22 appeared in a stripe pattern can be clearly observed and it is thus understood that the layers having steep interface are formed with a highly accurate film thickness.

FIG. 5B is a graph of XRD 2θ-θ spectrum showing the X-ray diffraction measurement result of the crystal laminate structure 2A shown in FIG. 5A. This graph clearly shows the peak 1 a due to the epitaxial growth substrate 1, plural satellite peaks 21 a due to the plural (AlGa)₂O₃ layers 21 and plural fringes 21 b therebetween and it is confirmed also from the X-ray diffraction measurement result that a crystal laminate structure having a steep interface is formed.

COMPARATIVE EXAMPLES

FIG. 6 are atomic force microscope images each showing a surface state of an epitaxial crystal as Comparative Example in case that an epitaxial crystal formed of β-Ga₂O₃ is grown by the same manufacturing method as mentioned above on the (100) plane or the (001) plane as the main surface of a β-Ga₂O₃-based single crystal substrate, wherein FIG. 6A shows a surface state when the (100) plane is the main surface and FIG. 6B shows a surface state when the (001) plane is the main surface. An arrow-B in FIG. 6A and FIG. 6B indicates a [010] direction of the substrate.

As shown in FIG. 6A and FIG. 6B, it is understood that needle-shaped crystals are grown in the [010] direction so as to be stacked in a direction vertical to the (100) plane or the (001) plane as the main surface in these Comparative Examples. This is considered a phenomenon caused because the growth rate in the [010] direction is faster than that in the [100] direction or the [001] direction.

The present inventors have also confirmed that, when elements other than Ga and O (e.g., Al, In, Si, Sn, Mg, Zn, etc.) are added while using the (100) plane or the (001) plane as the main surface, such elements are unevenly distributed at a portion of the epitaxial crystal since a relation between the substrate plane orientation and the growth rate is different depending on elements and a homogeneous epitaxial crystal thus cannot be obtained.

FIG. 7A is a transmission electron microscope observation image of a crystal laminate structure when plural (Al_(1-x)Ga_(x))₂O₃ layers (x=0.6) and plural Ga₂O₃ layers are alternately formed by epitaxial growth using the MBE system 3 on an epitaxial growth substrate formed of a β-Ga₂O₃-based single crystal having a (100) plane as a main surface. Meanwhile, FIG. 7B is a graph of XRD 2θ-θ spectrum showing the X-ray diffraction measurement result of the crystal laminate structure shown in FIG. 7A.

As shown in FIG. 7A, in this crystal laminate structure, an interface between the (Al_(1-x)Ga_(x))₂O₃ layer and the Ga₂O₃ layer is unclear and a stripe pattern such as shown in FIG. 5A is not observed. Meanwhile, the XRD 2θ-θ spectrum in FIG. 7B shows a peak 1 b due to diffraction from β-Ga₂O₃ (400) plane of the epitaxial growth substrate and plural peaks 23 a to 23 c which are observed therearound and are considered to be derived from the crystal laminate structure composed of the (Al_(1-x)Ga_(x))₂O₃ layers and the Ga₂O₃ layers. However, there is no periodicity in the intervals of these peaks and it is thus considered that a good laminate structure cannot be formed.

Effects of the First Embodiment

In the first embodiment, since the main surface 10 is the (010) plane of the epitaxial growth substrate 1 formed of β-Ga₂O₃-based single crystal, it is possible to provide a steep interface between the main surface 10 and the epitaxial crystal 20 formed thereon made of a Ga-containing oxide and it is also possible to form the epitaxial crystal 20 with a highly accurate thickness. In addition, it is possible to homogenize the epitaxial crystal 20 by suppressing unevenness in an amount of element incorporated thereinto.

Modification of the First Embodiment

Next, a modification of the first embodiment of the invention will be described in reference to FIG. 8.

FIG. 8A is a perspective view showing an epitaxial growth substrate 1B in the modification of the first embodiment. The epitaxial growth substrate 1B is formed of a β-Ga₂O₃-based single crystal in the same manner as the above-mentioned epitaxial growth substrate 1 but is different from the above-mentioned epitaxial growth substrate 1 in that a (310) plane is a main surface 10B.

FIG. 8B is a sterical view showing the (310) plane of the β-Ga₂O₃-based single crystal. Meanwhile, FIG. 8C is a diagram illustrating an angle δ formed between the (310) plane and the (010) plane of the β-Ga₂O₃-based single crystal. As shown in these drawings, the (310) plane of the β-Ga₂O₃-based single crystal is a plane which is inclined at an angle δ=37.5° with respect to the (010) plane.

It is possible to obtain a crystal laminate structure by forming the epitaxial crystal 20 on the main surface 10B (the (310) plane) of this epitaxial growth substrate 1B using the same method as described above.

FIG. 9 is an atomic force microscope image when observing a surface of the epitaxial crystal 20 which is formed on the main surface 10B of the epitaxial growth substrate 1B using the method described above. An arrow-C in the drawing indicates a c-axis direction.

As shown in this drawing, the epitaxial crystal 20 does not grow in a needle shape but is formed to extend in a direction crossing the main surface 10B.

Also in case of using this epitaxial growth substrate 1B, it is possible to obtain a crystal laminate structure which has a steep interface and allows the epitaxial crystal 20 to be formed with a highly accurate thickness. In addition, it is possible to homogenize the epitaxial crystal 20 by suppressing unevenness in an amount of element incorporated thereinto. In other words, it is possible to achieve the same effects as those described in the first embodiment even by the epitaxial growth substrate of which main surface is a plane inclined at an angle equal to or smaller than 37.5° with respect to the (010) plane.

Second Embodiment

Next, the second embodiment of the invention will be described in reference to FIG. 10. FIG. 10 is a cross sectional view showing an example structure of a high-electron-mobility transistor (HEMT) which is an example of the semiconductor device in the present embodiment.

In this high-electron-mobility transistor 4, the epitaxial growth substrate 1 in the first embodiment is provided as an element substrate and an i-type β-(AlGa)₂O₃ layer 41 as a first Ga-containing oxide layer and an n-type β-(AlGa)₂O₃ layer 42 as a second Ga-containing oxide layer are laminated by epitaxial growth on the main surface 10 of the epitaxial growth substrate 1. In addition, a gate electrode 43 g, a source electrode 43 s and a drain electrode 43 d are provided on the n-type β-(AlGa)₂O₃ layer 42.

The gate electrode 43 g is in contact with a surface 42 a of the n-type β-(AlGa)₂O₃ layer 42, thereby forming a Schottky junction. Meanwhile, the source electrode 43 s and the drain electrode 43 d are arranged with the gate electrode 43 g interposed therebetween and are in ohmic contact with the surface 42 a of the n-type β-(AlGa)₂O₃ layer 42.

While the β-(AlGa)₂O₃ single crystal generally has an n-type conductivity due to oxygen defects, the epitaxial growth substrate 1 in the second embodiment is doped with a predetermined amount of group II elements such as Mg and is thus formed to have high resistance.

The i-type β-(AlGa)₂O₃ layer 41 is an undoped electron transit layer and is formed by epitaxial growth on the main surface 10 of the epitaxial growth substrate 1. It is possible to form the i-type β-(AlGa)₂O₃ layer 41 by mixing, e.g., not less than 5 percent by weight of ozone to the oxygen gas supplied from the gas supply pipe 35.

The n-type β-(AlGa)₂O₃ layer 42 is an electron supply layer doped with a donor such as Si or Sn and is formed by epitaxial growth on the i-type β-(AlGa)₂O₃ layer 41.

Since the i-type β-(AlGa)₂O₃ layer 41 and the n-type β-(AlGa)₂O₃ layer 42 have different band gaps, discontinuity of bands occurs at the interface therebetween, electrons generated from the donor in the n-type β-(AlGa)₂O₃ layer 42 are concentrated on the i-type β-(AlGa)₂O₃ layer 41 side and are distributed in a region in the vicinity of the interface, and an electron layer called two-dimensional electron gas is thereby formed.

As such, a first depletion layer due to the Schottky junction of the gate electrode 43 g and a second depletion layer due to the formation of two-dimensional electron gas are produced in the n-type β-(AlGa)₂O₃ layer 42. The n-type β-(AlGa)₂O₃ layer 42 is formed in a thickness at which the first depletion layer is in contact with the second depletion layer.

Voltage is applied to the gate electrode 43 g to change the thicknesses of the first and second depletion layers and to adjust the concentration of the two-dimensional electron gas, thereby allowing drain current to be controlled.

The thickness of the i-type β-(AlGa)₂O₃ layer 41 is not specifically limited but is desirably not less than 0.1 nm. In addition, the thickness of the n-type β-(AlGa)₂O₃ layer 42 is set to 0.1 nm to 10 μm depending on a doping concentration.

Effects of the Second Embodiment

In the second embodiment, the i-type β-(AlGa)₂O₃ layer 41 having a steep interface with a highly accurate thickness can be formed on the main surface 10 which is the (010) plane of the β-Ga₂O₃-based single crystal constituting the epitaxial growth substrate 1 and, as a result, it is possible to provide a steep interface between the i-type β-(AlGa)₂O₃ layer 41 and the n-type β-(AlGa)₂O₃ layer 42. In addition, it is possible to form the n-type β-(AlGa)₂O₃ layer 42 with a highly accurate thickness. It is therefore possible to produce the high-electron-mobility transistor 4 with high performance and stable quality.

Third Embodiment

Next, the third embodiment of the invention will be described in reference to FIG. 11. FIG. 11 is a cross sectional view showing an example structure of a MESFET (Metal-Semiconductor Field Effect Transistor) which is one type of field-effect transistors and is another example of the semiconductor device in the present embodiment.

In this MESFET 5, the epitaxial growth substrate 1 in the first embodiment is provided as an element substrate and an n-type β-Ga₂O₃ layer 51 formed by epitaxial growth is provided on the main surface 10 (the (010) plane) of the epitaxial growth substrate 1. In addition, a gate electrode 52 g, a source electrode 52 s and a drain electrode 52 d are provided on the n-type β-Ga₂O₃ layer 51.

The gate electrode 52 g is in contact with a surface 51 a of the n-type β-Ga₂O₃ layer 51, thereby forming a Schottky junction. Meanwhile, the source electrode 52 s and the drain electrode 52 d are arranged with the gate electrode 52 g interposed therebetween and are in ohmic contact with the surface 51 a of the n-type β-Ga₂O₃ layer 51.

In the n-type β-Ga₂O₃ layer 51, the donor concentration is high in the vicinity of contact areas with the source electrode 52 s and with the drain electrode 52 d because of addition of Si or Sn, etc. Meanwhile, the donor concentration in the other region including a contact area with the gate electrode 52 g is lower than in the vicinity of the contact areas with the source electrode 52 s and with the drain electrode 52 d.

The epitaxial growth substrate 1 in the third embodiment is doped with a predetermined amount of group II elements such as Mg and is thus formed to have high resistance.

In the MESFET 5 configured as described above, the thickness of the depletion layer in the n-type β-Ga₂O₃ layer 51 is changed by adjusting bias voltage applied to the gate electrode 52 g, thereby allowing drain current to be controlled.

Effects of the Third Embodiment

In the third embodiment, the n-type β-Ga₂O₃ layer 51 having a steep interface a highly accurate thickness can be formed on the main surface 10 which is the (010) plane of the β-Ga₂O₃-based single crystal constituting the epitaxial growth substrate 1. Therefore, it is possible to produce the MESFET 5 with high performance and stable quality.

Fourth Embodiment

Next, the fourth embodiment of the invention will be described in reference to FIG. 12. FIG. 12 is a cross sectional view showing an example structure of a Schottky-barrier diode which is another example of the semiconductor device in the present embodiment.

In this Schottky-barrier diode 6, the epitaxial growth substrate 1 in the first embodiment is provided as an element substrate and an n-type β-Ga₂O₃ layer 61 formed by epitaxial growth is provided on the main surface 10 (the (010) plane) of the epitaxial growth substrate 1.

A Schottky electrode 62 is provided on the n-type β-Ga₂O₃ layer 61 and is in

Schottky-contact with a surface 61 a of the n-type β-Ga₂O₃ layer 61. Meanwhile, an ohmic electrode 63 is provided on a surface of the epitaxial growth substrate 1 opposite to the n-type β-Ga₂O₃ layer 61 and is ohmic contact with the epitaxial growth substrate 1.

In addition, the epitaxial growth substrate 1 in the fourth embodiment is formed to have an n-type conductivity by oxygen loss or impurity doping. The n-type β-Ga₂O₃ layer 61 is formed to have a lower donor concentration than the epitaxial growth substrate 1.

When forward voltage (electric potential is positive on the Schottky electrode 62 side) is applied to the Schottky diode 6, electric current is increased due to electron transfer from the epitaxial growth substrate 1 to the n-type β-Ga₂O₃ layer 61. As a result, a forward current flows from the Schottky electrode 62 to the ohmic electrode 63.

On the other hand, when reverse voltage (electric potential is negative on the Schottky electrode layer 2 side) is applied to the Schottky diode 6, substantially no electric current flows through the Schottky diode 6.

Effects of the Fourth Embodiment

In the fourth embodiment, the n-type β-Ga₂O₃ layer 61 having a steep interface with a highly accurate thickness can be formed on the main surface 10 which is the (010) plane of the β-Ga₂O₃-based single crystal constituting the epitaxial growth substrate 1. Therefore, it is possible to produce the Schottky diode 6 with high performance and stable quality.

Other Embodiments

Although the preferred embodiments of the invention have been described above, the present invention is not intended to be limited to these embodiments, and the various kinds of modifications and applications can be implemented without departing from the gist thereof.

Although, for example, the main surface is the (010) plane or the (310) plane of the β-Ga₂O₃-based single crystal in the above-mentioned first embodiment and the modification thereof, the main surface may be a plane between the (010) plane and the (310) plane. Alternatively, the main surface may be a plane inclined at an angle equal to or smaller than 37.5° in a direction other than the direction between the (010) plane and the (310) plane.

In addition, although the i-type β-(AlGa)₂O₃ layer 41 is formed on the epitaxial growth substrate 1 having the (010) plane as the main surface 10 in the second embodiment, the high-electron-mobility transistor may be formed by providing the i-type β-(AlGa)₂O₃ layer 41 on the epitaxial growth substrate 1B having the (310) plane as the main surface 10B. Furthermore, the main surface may be a plane inclined at an angle equal to or smaller than 37.5° from the (010) plane and the i-type 3-(AlGa)₂O₃ layer 41 may be formed on such a main surface.

In addition, although the n-type β-Ga₂O₃ layer 51/the n-type β-Ga₂O₃ layer 61 is formed on the epitaxial growth substrate 1 having the (010) plane as the main surface 10 in the third/fourth embodiment, the main surface may be a plane inclined at an angle equal to or smaller than 37.5° from the (010) plane and the n-type β-Ga₂O₃ layer 51/the n-type β-Ga₂O₃ layer 61 may be formed on such a main surface.

In addition, although the case where the invention is applied to the epitaxial growth substrate of the high-electron-mobility transistor, the MESFET and the Schottky-barrier diode has been described in the second to fourth embodiments, semiconductor devices to which the invention is applied are not limited thereto.

INDUSTRIAL APPLICABILITY

An epitaxial growth substrate, which allows an improvement in the crystalline quality of a Ga-containing oxide layer formed on the β-Ga₂O₃ single crystal substrate, and a crystal laminate structure are provided.

REFERENCE SIGNS LIST

1, 1B: epitaxial growth substrate

2, 2A: crystal laminate structure

3: MBE system

4: high-electron-mobility transistor

5: MESFET

6: Schottky-barrier diode

10, 10B: main surface

20: epitaxial crystal

20 a: satellite peak

21: (AlGa)₂O₃ layer

21 a: satellite peak

21 b: fringe peak 21 b

22: Ga₂O₃ layer

30: vacuum chamber

31: substrate holder

32: heating device

33 (33 a to 33 d): cell

34 (34 a to 34 d): heater

35: gas supply pipe

36: vacuum pump

41: i-type β-(AlGa)₂O₃ layer

42: n-type β-(AlGa)₂O₃ layer

42 a: surface

43 d: drain electrode

43 g: gate electrode

43 s: source electrode

51: n-type β-Ga₂O₃ layer

52 d: drain electrode

52 g: gate electrode

52 s: source electrode

61: n-type β-Ga₂O₃ layer

62: Schottky electrode

63: ohmic electrode

310: shaft 

1. An epitaxial growth substrate, comprising: a β-Ga₂O₃-based single crystal; and a (010) plane or a plane inclined at an angle not more than 37.5° with respect to the (010) plane as a main surface thereof.
 2. The epitaxial growth substrate according to claim 1, wherein the main surface comprises a (010) plane or a plane between the (010) plane and a (310) plane of the β-Ga₂O₃-based single crystal.
 3. The epitaxial growth substrate according to claim 2, wherein the main surface comprises the (010) plane or the (310) plane of the β-Ga₂O₃-based single crystal.
 4. A crystal laminate structure, comprising: an epitaxial growth substrate comprising a β-Ga₂O₃-based single crystal and a (010) plane or a plane inclined at an angle not more than 37.5° with respect to the (010) plane as a main surface thereof; and an epitaxial crystal formed on the main surface of the epitaxial growth substrate and comprising a Ga-containing oxide.
 5. The crystal laminate structure according to claim 4, wherein the main surface comprises a (010) plane or a plane between the (010) plane and a (310) plane of the β-Ga₂O₃-based single crystal.
 6. The crystal laminate structure according to claim 5, wherein the main surface comprises the (010) plane or the (310) plane of the β-Ga₂O₃-based single crystal. 